Semiconductor structure with enlarged gate electrode structure and method for forming the same

ABSTRACT

A semiconductor structure and a method for forming the same are provided. The semiconductor structure includes a gate stack structure formed over a substrate. The gate stack structure includes a gate electrode structure having a first portion and a second portion and a first conductive layer below the gate electrode structure. In addition, the first portion of the gate electrode structure is located over the second portion of the gate electrode structure, and a width of a top surface of the first portion of the gate electrode structure is greater than a width of a bottom surface of the second portion of the gate electrode structure.

PRIORITY DATA

The present application is a continuation application of U.S. patent application Ser. No. 15/687,308, filed Nov. 27, 2018, issuing as U.S. Pat. No. 10,141,416, which is a continuation application of U.S. patent application Ser. No. 14/927,842, filed Oct. 30, 2015, issuing as U.S. Pat. No. 9,748,350, entitled “SEMICONDUCTOR STRUCTURE WITH ENLARGED GATE ELECTRODE STRUCTURE AND METHOD FOR FORMING THE SAME”, which is hereby incorporated by reference in its entirety.

BACKGROUND

Semiconductor devices are used in a variety of electronic applications, such as personal computers, cell phones, digital cameras, and other electronic equipment. Semiconductor devices are typically fabricated by sequentially depositing insulating or dielectric layers, conductive layers, and semiconductor layers of material over a semiconductor substrate, and patterning the various material layers using lithography to form circuit components and elements thereon.

One of the important drivers for increased performance in a semiconductor structure is the higher levels of integration of circuits. This is accomplished by miniaturizing or shrinking device sizes on a given chip. Tolerances play an important role in being able to shrink dimensions on a chip.

However, although existing semiconductor manufacturing processes have generally been adequate for their intended purposes, as device scaling-down continues, they have not been entirely satisfactory in all respects.

BRIEF DESCRIPTION OF THE DRAWINGS

Aspects of the present disclosure are best understood from the following detailed description when read with the accompanying figures. It should be noted that, in accordance with the standard practice in the industry, various features are not drawn to scale. In fact, the dimensions of the various features may be arbitrarily increased or reduced for clarity of discussion.

FIGS. 1A to 1P are perspective views of various stages of forming a semiconductor structure in accordance with some embodiments.

FIG. 2 is a cross-sectional representation of the semiconductor structure illustrated along line A-A′ shown in FIG. 1P in accordance with some embodiments.

FIGS. 3A to 3B are cross-section representations of forming a semiconductor structure in accordance with some embodiments.

FIGS. 4A to 4B are cross-section representations of forming a semiconductor structure 100 c in accordance with some embodiments.

FIGS. 5A to 5B are cross-section representations of forming a semiconductor structure in accordance with some embodiments.

FIGS. 6A to 6D are cross-sectional representations of various stages of forming a semiconductor structure in accordance with some embodiments.

DETAILED DESCRIPTION

The following disclosure provides many different embodiments, or examples, for implementing different features of the invention. Specific examples of components and arrangements are described below to simplify the present disclosure. These are, of course, merely examples and are not intended to be limiting. For example, the formation of a first feature over or on a second feature in the description that follows may include embodiments in which the first and second features are formed in direct contact, and may also include embodiments in which additional features may be formed between the first and second features, such that the first and second features may not be in direct contact. In addition, the present disclosure may repeat reference numerals and/or letters in the various examples. This repetition is for the purpose of simplicity and clarity and does not in itself dictate a relationship between the various embodiments and/or configurations discussed.

Further, spatially relative terms, such as “beneath,” “below,” “lower,” “above,” “upper” and the like, may be used herein for ease of description to describe one element or feature's relationship to another element(s) or feature(s) as illustrated in the figures. The spatially relative terms are intended to encompass different orientations of the device in use or operation in addition to the orientation depicted in the figures. The apparatus may be otherwise oriented (rotated 90 degrees or at other orientations) and the spatially relative descriptors used herein may likewise be interpreted accordingly.

Embodiments of semiconductor structures and methods for forming the same are provided. The semiconductor structure may include a gate stack structure including a conductive layer and a gate electrode structure formed over the conductive layer. Before the gate electrode structure is formed, some portions of the conductive layer are etched back, so that the space for forming the gate electrode structure can be enlarged.

FIGS. 1A to 1P are perspective views of various stages of forming a semiconductor structure 100 a in accordance with some embodiments. As shown in FIG. 1A, a substrate 102 is received in accordance with some embodiments. Substrate 102 may be a semiconductor wafer such as a silicon wafer. Alternatively or additionally, substrate 102 may include elementary semiconductor materials, compound semiconductor materials, and/or alloy semiconductor materials. Examples of the elementary semiconductor materials may be, but are not limited to, crystal silicon, polycrystalline silicon, amorphous silicon, germanium, and/or diamond. Examples of the compound semiconductor materials may be, but are not limited to, silicon carbide, gallium arsenic, gallium phosphide, indium phosphide, indium arsenide, and/or indium antimonide. Examples of the alloy semiconductor materials may be, but are not limited to, SiGe, GaAsP, AlInAs, AlGaAs, GaInAs, GaInP, and/or GaInAsP.

In addition, substrate 102 may include structures such as doped regions, interlayer dielectric (ILD) layers, conductive features, and/or isolation structures. Furthermore, substrate 102 may further include single or multiple material layers to be patterned. For example, the material layers may include a silicon layer, a dielectric layer, and/or a doped poly-silicon layer.

A dielectric layer 104 and a mask layer 106 are formed over substrate 102, and a photo-sensitive layer 108 is formed over mask layer 104, as shown in FIG. 1A in accordance with some embodiments. Dielectric layer 104 may be used as an adhesion layer between substrate 102 and mask layer 106. In addition, dielectric layer 104 may also be used as an etch stop layer for etching mask layer 106. In some embodiments, dielectric layer 104 is made of silicon oxide. Dielectric layer 104 may be formed by using a thermal oxidation process, although other deposition processes may be used in some other embodiments.

Mask layer 106 may be used as a hard mask during subsequent photolithography processes. In some embodiments, mask layer 106 is made of silicon nitride. Mask layer 106 may be formed by using low-pressure chemical vapor deposition (LPCVD) or plasma enhanced chemical vapor deposition (PECVD), although other deposition processes may also be used in some other embodiments.

Next, a fin structure 110 is formed by sequentially etching mask layer 106, dielectric layer 104, and substrate 102 through photo-sensitive layer 108, as shown in FIG. 1B in accordance with some embodiments. Afterwards, photo-sensitive layer 108 is removed.

After fin structure 110 is formed, an insulating layer 112 is formed to cover fin structures 110 over substrate 102, as shown in FIG. 1C in accordance with some embodiments. In some embodiments, insulating layer 112 is made of silicon oxide, silicon nitride, silicon oxynitride, fluoride-doped silicate glass (FSG), or other low-K dielectric materials. Insulating layer 112 may be formed by using a high-density-plasma (HDP) CVD process, although other deposition processes may be used in other embodiments.

Next, insulating layer 112 is recessed to form an isolation structure 114, such as a shallow trench isolation structure, around fin structure 110, as shown in FIG. 1D in accordance with some embodiments. Insulating layer 112 may be recessed by a wet etching process or a dry etching process. In addition, mask layer 106 and dielectric layer 104 are removed.

Afterwards, a dummy gate structure 116 is formed across fin structure 110 and extends over isolation structure 114. In some embodiments, dummy gate structure 116 includes a dummy gate dielectric layer 118 and a dummy gate electrode layer 120 formed over dummy gate dielectric layer 118. In some embodiments, dummy gate dielectric layer 118 is made of silicon oxide. In some embodiments, dummy gate electrode layer 120 is made of polysilicon.

After dummy gate structure 116 is formed, spacers 122 are formed on the sidewalls of dummy gate structure 116 in accordance with some embodiments. In some embodiments, spacers 122 are made of silicon nitride, silicon oxide, silicon oxynitride, silicon carbide, or other applicable dielectric materials. Spacers 122 may include a single layer or multiple layers.

Next, source/drain structures 124 are formed in fin structure 110, as shown in FIG. 1E in accordance with some embodiments. In some embodiments, portions of fin structure 110 adjacent to dummy gate structure 116 are recessed to form recesses at two sides of fin structure 110, and a strained material is grown in the recesses by an epitaxial (epi) process to form source/drain structures 124. In addition, the lattice constant of the strained material may be different from the lattice constant of substrate 102. In some embodiments, source/drain structures 124 include Ge, SiGe, InAs, InGaAs, InSb, GaAs, GaSb, InAlP, InP, or the like.

After source/drain structures 124 are formed, a contact etch stop layer (CESL) 126 is formed over substrate 102, and an inter-layer dielectric (ILD) layer 128 is formed over contact etch stop layer 126, as shown in FIG. 1F in accordance with some embodiments. In some embodiments, contact etch stop layer 126 is made of silicon nitride, silicon oxynitride, and/or other applicable materials. Contact etch stop layer 126 may be formed by plasma enhanced CVD, low pressure CVD, ALD, or other applicable processes.

Inter-layer dielectric layer 128 may include multilayers made of multiple dielectric materials, such as silicon oxide, silicon nitride, silicon oxynitride, phosphosilicate glass (PSG), borophosphosilicate glass (BPSG), and/or other applicable low-k dielectric materials. Inter-layer dielectric layer 128 may be formed by chemical vapor deposition (CVD), physical vapor deposition, (PVD), atomic layer deposition (ALD), spin-on coating, or other applicable processes.

Next, a polishing process is performed on inter-layer dielectric layer 128 and contact etch stop layer 126 to expose the top surface of dummy gate structure 116 in accordance with some embodiments. In some embodiments, a chemical mechanical polishing (CMP) process is performed until the top surface of dummy gate structure 116 is exposed.

After the polishing process is performed, dummy gate structure 116 is removed, such that a trench 130 a is formed, as shown in FIG. 1G in accordance with some embodiments. As shown in FIG. 1G, trench 130 a is formed in interlayer dielectric layer 128 over substrate 102. In some embodiments, dummy gate structure 116 is removed by performing a dry etching process. In some embodiments, dummy gate structure 116 is removed by performing a dry etching process and a wet etching process. In order to miniaturize or shrink device sizes on a given substrate, the dummy gate may have a relatively small width. Therefore, the resulting trench 130 a may also have a relatively small width. In some embodiments, trench 130 a has a width in a range from about 10 nm to about 25 nm.

After dummy gate structure 116 is removed, a gate dielectric layer 132 is formed lining trench 130 a, as shown in FIG. 1H in accordance with some embodiments. As shown in FIG. 1H, gate dielectric layer 132 is formed the sidewalls and the bottom surface of trench 130 a. In some embodiments, gate dielectric layer 132 is made of silicon oxide. In some embodiments, gate dielectric layer 132 is made of high-k dielectric materials, such as metal oxides, metal nitrides, metal silicates, transition metal-oxides, transition metal-nitrides, transition metal-silicates, or oxynitrides of metals. Examples of the high-k dielectric material include, but are not limited to, hafnium oxide (HfO₂), hafnium silicon oxide (HfSiO), hafnium silicon oxynitride (HfSiON), hafnium tantalum oxide (HfTaO), hafnium titanium oxide (HfTiO), hafnium zirconium oxide (HfZrO), zirconium oxide, titanium oxide, aluminum oxide, hafnium dioxide-alumina (HfO₂—Al₂O₃) alloy, or other applicable dielectric materials.

Afterwards, a conductive layer 134 is formed over gate dielectric layer 132, as shown in FIG. 1H in accordance with some embodiments. As shown in FIG. 1H, conductive layer 134 is formed over the sidewalls and the bottom of trench 130. In some embodiments, conductive layer 134 is a metal layer. In some embodiments, conductive layer 134 is made of a work function metal, which is configured to have a proper work function. In some embodiments, conductive layer 134 is made of Ti_(x)N_(y), W, Ti_(x)Al_(y), Ti_(x)Al_(y)N, Ta_(x)Al_(y), Ta_(x)Al_(y)N_(z), Ti_(x)Si_(y)N_(z), Ta_(x)Si_(y)N_(z), Ta_(x)N_(y), Hf_(x)O_(y), Ti_(x)Ta_(y)N_(z). In some embodiments, conductive layer 134 has a thickness in a range from about 1 Å to about 500 Å.

After conductive layer 134 is formed, another conductive layer 136 is formed over conductive layer 134, as shown in FIG. 1H in accordance with some embodiments. In some embodiments, conductive layer 134 and conductive layer 136 are made of different materials. In some embodiments, conductive layer 134 and conductive layer 136 are made of different materials which have relative high etching selectivity in a wet etching process.

In some embodiments, conductive layer 136 is a metal layer. In some embodiments, conductive layer 136 is made of a work function metal, which is configured to have a proper work function. In some embodiments, conductive layer 136 is made of Ti_(x)N_(y), W, Ti_(x)Al_(y), Ti_(x)Al_(y)N, Ta_(x)Al_(y), Ta_(x)Al_(y)N_(z), Ti_(x)Si_(y)N_(z), Ta_(x)Si_(y)N_(z), Ta_(x)N_(y), Hf_(x)O_(y), Ti_(x)Ta_(y)N_(z). In some embodiments, conductive layer 136 has a thickness in a range from about 1 Å to about 500 Å.

After conductive layers 134 and 136 are formed, a hard mask layer 138 a is formed over conductive layer 136, as shown in FIG. 1I in accordance with some embodiments. As shown in FIG. 1I, trench 130 a is filled with hard mask layer 138. In some embodiments, hard mask layer 138 is made of carbon-based materials, oxide based materials, silicon based materials, or combinations thereof.

Next, a first etching process 140 a is performed on hard mask layer 138, as shown in FIG. 1J in accordance with some embodiments. In some embodiments, first etching process 140 a is a dry etching process. During first etching process 140 a, the portion of hard mask layer 138 a positioned in the upper portion of trench 130 a is removed, so that a blocking structure 142 a is formed, as shown in FIG. 1J in accordance with some embodiments. After first etching process 140 a, blocking structure 142 a is formed in the lower portion of trench 130 a, such that the portion of conductive layer 136 formed at the lower portion of trench 130 a is covered by blocking structure 142 a while the portion of conductive layer 136 formed at the upper portion 131 a of trench 130 a are exposed.

After blocking structure 142 a is formed, the portion of conductive layer 136 which is not covered by blocking structure 142 a is etched by a second etching process 144 a, as shown in FIG. 1K in accordance with some embodiments. In some embodiments, second etching process 144 a is a wet etching process. As described previously, conductive layers 134 and 136 are made of different materials. However, since conductive layers 134 and 136 are both made of conductive materials such as metals, they may have poor etching selectivity in a dry etching process. Therefore, a wet etching process is performed to remove the portion of conductive layer 136 not covered by blocking structure 142 a, so that only a small amount of conductive layer 134 formed below conductive layer 136 will be etched during the wet etching process in accordance with some embodiments.

In addition, when conductive layer 136 is etched by performing second etching process 144, which is a wet etching process, conductive layer 136 has a sloped (inclined) top surface. The sloped top surface may enable the filling of gate electrode material become easier (Details will be described later.)

After second etching process 144 a is performed, blocking structure 142 a is removed to expose lower portion 133 a of trench 130 a, as shown in FIG. 1L in accordance with some embodiments. As shown in FIG. 1L, after blocking structure 142 a is removed, trench 130 a has a funnel shape with a wider upper portion 131 a in a cross-sectional view.

Next, a gate electrode layer 146 a is formed over substrate 102, as shown in FIG. 1M in accordance with some embodiments. More specifically, gate electrode layer 146 a is formed over conductive layers 134 and 136, and upper portion 131 a and lower portion 133 a of trench 130 a are both filled with gate electrode layer 146 a. As described previously, since trench 130 a has a wider upper portion and conductive layer 134 has the sloped top surface, it may be easier for gate electrode layer 146 a to be formed in trench 130 a. In some embodiments, gate electrode layer 146 a is made of a conductive material, such as tungsten, aluminum, copper, titanium, tantulum, or other applicable materials.

After gate electrode layer 146 a is formed, a polishing process is performed until the top surface of interlayer dielectric layer 128 is exposed, as shown in FIG. 1N in accordance with some embodiments. In some embodiments, the polishing process is a chemical mechanical polishing process. As shown in FIG. 1N, a gate electrode structure 148 a is formed. Since gate electrode structure 148 a is formed in trench 130 a, gate electrode structure 148 a also has a funnel shape in its cross-sectional view in accordance with some embodiments. In addition, conductive layer 134, conductive layer 136, and gate electrode structure 148 a can be seen as a gate stack structure 150 a.

Afterwards, an etching-back process is performed on gate stack structure 150 a, as shown in FIG. 1O in accordance with some embodiments. During the etching-back process, the upper portion of gate electrode structure 148 a and the upper portions of conductive layer 134 are etched. A recess 152 is formed after the etching-back process is performed. Next, a hard mask structure 154 is formed in trench 152, as shown in FIG. 1P in accordance with some embodiments. In some embodiments, hard mask structure 154 formed over gate stack structure 150 and is made of silicon nitride.

FIG. 2 is a cross-sectional representation of semiconductor structure 100 a illustrated along line A-A′ shown in FIG. 1P in accordance with some embodiments. As shown in FIG. 2, semiconductor structure 100 a includes gate stack structure 150 a formed across fin structure 110, and gate stack structure 150 a includes conductive layer 134, conductive layer 136, and gate electrode structure 148 a.

As described previously, dummy gate structure 116 (as shown in FIG. 1F) may have a relatively small width for device size shrinkage, and therefore gate stack structure 150 a may also have a relatively small width. In some embodiments, gate stack structure 150 a has a width in a range from about 10 nm to about 25 nm. However, although the width of gate stack structure 150 a is relatively small, the size of gate electrode structure 148 a can still be relatively large since second etching process 144 a is performed to remove the upper portion of conductive layer 136 so that the space for forming gate electrode structure 148 a is enlarged.

As shown in FIG. 2, gate electrode structure 148 a has a funnel shape in its cross-sectional view in accordance with some embodiments. In addition, gate electrode structure 148 a includes a first portion 156 a, a second portion 158 a, and a third portion 160 a in accordance with some embodiments. First portion 156 a is located over second portion 158 a, and second portion 158 a is located over third portion 160 a. In some embodiments, second portion 158 a has a trapezoid shape in its cross-sectional view.

As shown in FIG. 2, conductive layer 136 is formed around second portion 158 a and third portion 160 a but is not formed over the sidewalls of first portion 156 a of gate electrode structure 148 a in accordance with some embodiments. In addition, conductive layer 134 is located around conductive layer 136 and extends over the sidewalls of first portion 156 a in accordance with some embodiments.

As described previously, second etching process 144 a is performed, so that gate electrode structure 148 a can have a wide upper portion (e.g. first portion 156 a.) As shown in FIG. 2, the width of the top surface of gate electrode structure 148 a (e.g. the width of the top surface of first portion 156 a) is greater than the width of the bottom surface of gate electrode structure 148 a (e.g. the width of the bottom surface of third portion 160 a or the width of the bottom surface of second portion 158 a) in accordance with some embodiments. In some embodiments, the width of the top surface of first portion 156 a is greater than the width of the bottom surface of second portion 158 a.

In some embodiments, the width of the top surface of gate electrode structure 148 a is in a range from about 5 nm to about 300 nm. In some embodiments, the width of the bottom surface of gate electrode structure 148 a is in a range from 1 Å to about 300 nm. As described previously, the upper portions of conductive layer 136 is removed, so the space for forming gate electrode structure 148 e is enlarged and has a greater upper portion. Therefore, gate electrode structure 148 e formed in the enlarged spacer also has the larger upper portion (e.g. first portion 156 a), and the resistance of gate stack structure 150 a may be reduced accordingly.

Furthermore, since second etching process 144 a is performed, conductive layer 136 has the sloped top surface, which can also be seen as the sidewall of second portion 158 a of gate electrode structure 148 a. As shown in FIG. 2, the sidewall of first portion 156 a has a first inclination, the sidewall of second portion 158 a has a second inclination, and the sidewall of third portion 160 a has a third inclination. The first inclination, the second inclination, and the third inclination are different from one another in accordance with some embodiments.

In some embodiments, an angle between the sidewall of first portion 156 a and the sidewall of second portion 158 a is in a range from about 95° to about 175°. In some embodiments, an angle between the sidewall of second portion 158 a and the sidewall of third portion 160 a is in a range from about 95° to about 175°. Gate electrode structure 148 a is formed with such a shape, so that the filling of gate electrode layer 146 a can be easier and the risk of forming gaps during the depositing process may be reduced.

In some embodiments, first portion 156 a has a thickness T₁ in a range from about 0 nm to about 100 nm. In some embodiments, first portion 156 a has a thickness T₁ in a range from about 2 nm to about 100 nm. In some embodiments, second portion 158 a has a thickness T₂ in a range from about 2 nm to about 50 nm. In some embodiments, third portion 160 a has a thickness T₃ in a range from about 2 nm to about 50 nm. By performing second etching process 144 a, the size of gate electrode structure 148 a may also be enlarged, and the resistance of the resulting gate stack structure 150 a can be reduced.

FIGS. 3A to 3B are cross-section representations of forming a semiconductor structure 100 b in accordance with some embodiments. Semiconductor structure 100 b is similar to semiconductor structure 100 a, except an additional conductive layer is formed. Materials and processes used to form semiconductor structure 100 b may be similar to, or the same as, those used to form semiconductor structure 100 a described previously and are not repeated herein.

More specifically, processes shown in FIGS. 1A to 1H may be performed. After conductive layer 134 and conductive layer 136 are formed in the trench 130 b, an additional conductive layer 236 is formed over conductive layer 136 in accordance with some embodiments. Next, a blocking structure 142 b may be formed at a lower portion 133 b of trench 130 b, and a second etching process 144 b may be performed. In some embodiments, second etching process 144 b is a wet etching process. During second etching process 144 b, conductive layer 236 and conductive layer 134 are both etched to enlarge the space for depositing a gate electrode layer later on. Afterwards, processes shown in FIGS. 1L to 1P may be performed to form semiconductor structure 100 b.

As shown in FIG. 3B, semiconductor structure 100 b includes a gate stack structure 150 b formed across fin structure 110 over a substrate (e.g. substrate 102), and gate stack structure 150 b includes conductive layer 134, conductive layer 136, conductive layer 236, and a gate electrode structure 148 b. Gate electrode structure 148 b includes a first portion 156 b, a second portion 158 b, and a third portion 160 b. In addition, hard mask structure 154 is formed over gate stack structure 150 b. In some embodiments, conductive layer 236 is made of Ti_(x)N_(y), W, Ti_(x)Al_(y), Ti_(x)Al_(y)N, Ta_(x)Al_(y), Ta_(x)Al_(y)N_(z), Ti_(x)Si_(y)N_(z), Ta_(x)Si_(y)N_(z), Ta_(x)N_(y), Hf_(x)O_(y), Ti_(x)Ta_(y)N_(z). In addition, conductive layers 134, 136, and 236 are made of different materials in accordance with some embodiments.

Since second etching process 144 b is performed to conductive layer 136 and conductive layer 236, conductive layer 136 and conductive layer 236 may have sloped top surfaces, which may help the deposition of the gate electrode layer formed thereon. In addition, by performing second etching process 144 b, the space for forming gate electrode structure 148 b is enlarged, and therefore gate electrode structure 148 b is enlarged. By forming gate stack structure 150 b having larger gate electrode structure 148 b, the resistance of gate stack structure 150 b can be reduced, and the performance of semiconductor structure 100 b may be improved.

FIGS. 4A to 4B are cross-section representations of forming a semiconductor structure 100 c in accordance with some embodiments. Semiconductor structure 100 c is similar to semiconductor structure 100 a, except both conductive layers are etched during the second etching process. Materials and processes used to form semiconductor structure 100 c may be similar to, or the same as, those used to form semiconductor structure 100 a described previously and are not repeated herein.

More specifically, processes shown in FIGS. 1A to 1J may be performed. After a blocking structure 142 c is formed in the lower portion of a trench 130 c over a conductive layer 134′ and conductive layer 136, a second etching process 144 c is performed in accordance with some embodiments. In some embodiments, conductive layer 134′ is made of Ti_(x)N_(y), W, Ti_(x)Al_(y), Ti_(x)Al_(y)N, Ta_(x)Al_(y), Ta_(x)Al_(y)N_(z), Ti_(x)Si_(y)N_(z), Ta_(x)Si_(y)N_(z), Ta_(x)N_(y), Hf_(x)O_(y), Ti_(x)Ta_(y)N_(z). In addition, conductive layers 134′ and 136 are made of different materials in accordance with some embodiments. During second etching process 144 c, both conductive layer 134′ and conductive layer 136 are etched. Afterwards, processes shown in FIGS. 1L to 1P may be performed.

As shown in FIG. 4B, semiconductor structure 100 c includes a gate stack structure 150 c formed across fin structure 110 over a substrate, and gate stack structure 150 c includes conductive layer 134′, conductive layer 136, and gate electrode structure 148 c. Gate electrode structure 148 c includes a first portion 156 c, a second portion 158 c, and a third portion 160 c. In addition, hard mask structure 154 is formed over gate stack structure 150 c.

Since second etching process 144 c is performed to both conductive layer 134′ and conductive layer 136, conductive layer 134′ and conductive layer 136 may both have sloped top surfaces. The sloped top surface may help the deposition of the gate electrode layer formed thereon. In addition, by performing second etching process 144 c, the space for forming gate electrode structure 148 c is enlarged, and therefore gate electrode structure 148 c formed in the space is enlarged. By forming gate stack structure 150 c having larger gate electrode structure 148 c, the resistance of gate stack structure 150 c can be reduced, and the performance of semiconductor structure 100 c may be improved.

FIGS. 5A to 5B are cross-section representations of forming a semiconductor structure 100 d in accordance with some embodiments. Semiconductor structure 100 d is similar to semiconductor structure 100 a, except only one conductive layer is formed. Materials and processes used to form semiconductor structure 100 d may be similar to, or the same as, those used to form semiconductor structure 100 a described previously and are not repeated herein.

More specifically, processes shown in FIGS. 1A to 1H may be performed. However, only one conductive layer 136′ is formed in a trench 130 d in accordance with some embodiments. In some embodiments, conductive layer 136′ is made of Ti_(x)N_(y), W, Ti_(x)Al_(y), Ti_(x)Al_(y)N, Ta_(x)Al_(y), Ta_(x)Al_(y)N_(z), Ti_(x)Si_(y)N_(z), Ta_(x)Si_(y)N_(z), Ta_(x)N_(y), Hf_(x)O_(y), Ti_(x)Ta_(y)N_(z). After conductive layer 136′ is formed, a blocking structure 142 d is formed in the lower portion of trench 130 d, and a second etching process 144 d is performed to etch the upper portion of conductive layer 136′. After second etching process 144 d is performed, process shown in FIGS. 1L to 1P may be performed.

As shown in FIG. 5B, semiconductor structure 100 d includes a gate stack structure 150 d formed across fin structure 110 over the substrate, and gate stack structure 150 d includes conductive layer 136′ and gate electrode structure 148 d. In addition, hard mask structure 154 is formed over gate stack structure 150 d.

Similarly, conductive layer 136′ also has sloped top surfaces and enlarged gate electrode structure 148 d, and therefore the resistance of gate stack structure 150 d can be reduced, and the performance of semiconductor structure 100 d may be improved.

FIGS. 6A to 6D are cross-sectional representations of various stages of forming a semiconductor structure 100 e in accordance with some embodiments. Some materials and processes used to form semiconductor structure 100 e may be similar to, or the same as, those used to form semiconductor structure 100 a and are not repeated herein.

A structure similar to that shown in FIG. 4A may be formed, and the method to form the structure may be similar to, or the same as, those described previously. More specifically, a dummy gate structure is formed across fin structure 110 over a substrate, and spacers 122, contact etch stop layer 126, and interlayer dielectric layer 128 are formed around the dummy gate structure. Next, the dummy gate structure is removed to form a trench 130 e between spacers 122, and a conductive layer 634 and a conductive layer 636 are formed over the bottom and the sidewalls of trench 130 e. In some embodiments, conductive layer 634 and conductive layer 636 are individually made of Ti_(x)N_(y), W, Ti_(x)Al_(y), Ti_(x)Al_(y)N, Ta_(x)Al_(y), Ta_(x)Al_(y)N_(z), Ti_(x)Si_(y)N_(z), Ta_(x)Si_(y)N_(z), Ta_(x)N_(y), Hf_(x)O_(y), Ti_(x)Ta_(y)N_(z). In some embodiments, conductive layer 634 and conductive layer 636 are made of different materials.

Afterwards, a blocking structure 142 e is formed in the lower portion of trench 130 e and a second etching process 144 e is performed to etch conductive layer 634 and conductive layer 636. As shown in FIG. 6A, after second etching process 144 e is performed, conductive layer 634 and conductive layer 636 have sloped top surfaces in accordance with some embodiments.

Next, block structure 142 e is removed, and trench 130 e now includes an upper region 130 e and a lower portion 133 e, as shown in FIG. 6B in accordance with some embodiments. As shown in FIG. 6B, lower portion 133 e of trench 130 e is surrounded by conductive layer 636. Afterwards, another conductive layer 638 is formed in trench 130 e, as shown in FIG. 6C in accordance with some embodiments. In some embodiments, conductive layer 638 is made of Ti_(x)N_(y), W, Ti_(x)Al_(y), Ti_(x)Al_(y)N, Ta_(x)Al_(y), Ta_(x)Al_(y)N_(z), Ti_(x)Si_(y)N_(z), Ta_(x)Si_(y)N_(z), Ta_(x)N_(y), Hf_(x)O_(y), Ti_(x)Ta_(y)N_(z). In some embodiments, conductive layers 634, 636, and 638 are made of different materials.

More specifically, conductive layer 638 covers the upper portion of the sidewalls of trench 130 e, the slopes top surfaces of conductive layer 634 and conductive layer 636, and the sidewalls of conductive layer 636. In some embodiments, lower portion 133 e of trench 130 e is fully filled with conductive layer 638. That is, conductive layer 638 has an extending portion surrounding by conductive layer 636 in accordance with some embodiments.

After conductive layer 638 is formed, processes similar to those shown in FIGS. 1M to 1P may be performed to form semiconductor structure 100 e. As shown in FIG. 6D, semiconductor structure 100 e includes a gate stack structure 150 e formed across fin structure 110 over the substrate, and gate stack structure 150 e includes conductive layer 346, conductive layer 636, conductive layer 638, and gate electrode structure 148 e. Gate electrode structure 148 e includes a first portion 156 e and a second portion 158 e. In addition, hard mask structure 154 is formed over gate stack structure 150 e.

In some embodiments, second portion 158 e has a tip bottom portion. In some embodiments, second portion 158 e has a triangular shape in its cross-sectional view. As shown in FIG. 6D, conductive layer 638 is positioned between conductive layer 636 and gate electrode structure 148 e and covers the sidewalls of first portion 156 e and second portion 158 e.

By performing second etching process 144 e, the upper portion of conductive layer 634 and conductive layer 636 are removed. Therefore, after conductive layer 638 is formed, upper portion 131 e of trench 130 e can still have enough space for forming gate electrode structure 148 e, although lower portion 133 e of trench 130 e is filled with conductive layer 638. Accordingly, even if the width of gate stack structure 150 e is relatively narrow, a number of conductive layers may still be formed in lower portion 131 e of trench and there will still be enough space for gate electrode structure 148 e to be formed.

It should be noted that although some structures shown in the figures and described previously are divided into several portions, they are drawn and described for better understanding the concept of the disclosure. However, there may not be actual boundaries or interfaces between them. In addition, in various embodiments, a gate stack structure may include one or more conductive layers, and the scope of the disclosure is not intended to be limiting.

As described previously, a gate stack structure (e.g. gate stack structure 150 a to 150 e) includes a conductive layer (e.g. conductive layers 134, 136, 236, 134′, 136′, 634, 636, and 638) and a gate electrode structure (e.g. gate electrode structures 148 a to 148 e) formed over the conductive layer in accordance with some embodiments. In addition, before the gate electrode structure is formed, an etching process (e.g. second etching processes 144 a to 144 e) is performed, so that the space for forming the gate electrode layer is enlarged. Therefore, the gate stack structure can have a larger gate electrode structure, such as made of tungsten, and therefore the resistance of the gate stack structure can be reduced.

In addition, a hard mask layer (e.g. hard mask layer 154) is formed over the gate stack structure in accordance with some embodiments. Since the etching process is performed to enlarge the space of the upper portion of the gate stack structure, there also is enough space for forming the hard mask layer. Therefore, the risk for forming short circuit due to thin hard mask layer can be reduced. In addition, even if the hard mask layer is formed, the remaining gate electrode structure can still have a sufficient size, and the performance of the gate stack structure may be improved.

Furthermore, in some embodiments, the etching process is a wet etching process. When several conductive layers are formed, the wet etching process may have a better etching selectively towards each conductive layer. In addition, after the etching process, the conductive layer may have a sloped top surface, which may help the forming of the gate electrode layer (e.g. gate electrode layer 146 a) formed over it. Moreover, by performing the wet etching process, the risks of shortening the gate stack height due to etching may also be reduced.

Embodiments of a semiconductor structure and methods for forming the semiconductor structures are provided. The semiconductor structure includes a gate stack structure. The gate stack structure includes a gate electrode structure and a conductive layer formed below the gate electrode structure. The gate electrode structure includes a wide upper portion and a narrow lower portion, so that the resistance of the gate stack structure may be reduced. Therefore, the performance of the gate stack structure may be improved.

In some embodiments, a semiconductor structure is provided. The semiconductor structure includes a gate stack structure formed over a substrate. The gate stack structure includes a gate electrode structure having a first portion and a second portion and a first conductive layer below the gate electrode structure. In addition, the first portion of the gate electrode structure is located over the second portion of the gate electrode structure, and a width of a top surface of the first portion of the gate electrode structure is greater than a width of a bottom surface of the second portion of the gate electrode structure.

In some embodiments, a semiconductor structure is provided. The semiconductor structure includes a fin structure formed over a substrate and a gate stack structure formed across the fin structure. the gate stack structure includes a gate electrode structure having a first portion, a second portion located below the first portion, and a third portion located below the second portion and a first conductive layer formed around the second portion and the third portion of the gate electrode structure. In addition, a width of a top surface of the first portion of the gate electrode layer is greater than a width of a bottom surface of the third portion of the gate electrode layer.

In some embodiments, a method for manufacturing a semiconductor structure is provided. The method for manufacturing a semiconductor structure includes forming a trench over a substrate and forming a first conductive layer on sidewalls and a bottom of the trench. The method for manufacturing a semiconductor structure further includes forming a hard mask layer over the first conductive layer and etching the hard mask layer to form a blocking structure in a lower portion of the trench by performing a first etching process. The method for manufacturing a semiconductor structure further includes etching a portion of the first conductive layer not covered by the blocking structure by performing a second etching process and removing the blocking structure. The method for manufacturing a semiconductor structure further includes filling the trench by a gate electrode layer.

The foregoing outlines features of several embodiments so that those skilled in the art may better understand the aspects of the present disclosure. Those skilled in the art should appreciate that they may readily use the present disclosure as a basis for designing or modifying other processes and structures for carrying out the same purposes and/or achieving the same advantages of the embodiments introduced herein. Those skilled in the art should also realize that such equivalent constructions do not depart from the spirit and scope of the present disclosure, and that they may make various changes, substitutions, and alterations herein without departing from the spirit and scope of the present disclosure. 

What is claimed is:
 1. A semiconductor structure, comprising: a gate structure formed over a semiconductor substrate, wherein the gate structure comprises: a gate dielectric layer; a first conductive layer over the gate dielectric layer; a second conductive layer over the first conductive layer, wherein the second conductive layer has a first inclined top surface and a second inclined top surface, wherein an incline of the first inclined top surface extends from a first point near the first conductive layer downward to a second point near a gate electrode layer and an incline of the second inclined top surface extends from a first point near the first conductive layer downward to a second point near the gate electrode layer; the gate electrode layer disposed over the second conductive layer; and a hard mask layer being in contact with the gate electrode layer and in contact with at least one of the first conductive layer or the gate dielectric layer.
 2. The semiconductor structure of claim 1, wherein the gate electrode layer has a funnel shape in a cross-sectional view.
 3. The semiconductor structure of claim 1, wherein the gate structure is formed over a fin structure.
 4. The semiconductor structure of claim 1, wherein the incline of the first inclined top surface and the incline of the second inclined top surface face one another.
 5. The semiconductor structure of claim 1, wherein the first conductive layer and the second conductive layer are comprised of a work function metal.
 6. The semiconductor structure of claim 1, wherein the hard mask layer contacts a sidewall of the gate dielectric layer, the sidewall extending substantially perpendicular to a top surface of the semiconductor substrate.
 7. The semiconductor structure of claim 6, wherein the first conductive layer and the second conductive layer are selected from a group that includes Ti_(x)N_(y), W, Ti_(x)Al_(y), Ti_(x)Al_(y)N, Ta_(x)Al_(y), Ta_(x)Al_(y)N_(z), Ti_(x)Si_(y)N_(z), Ta_(x)Si_(y)N_(z), Ta_(x)N_(y), Hf_(x)O_(y), and Ti_(x)Ta_(y)N_(z) and wherein the first conductive layer has a different composition than the second conductive layer.
 8. The semiconductor structure of claim 1, wherein the first conductive layer has a first portion of a top surface having an incline and a second portion of the top surface having an incline.
 9. The semiconductor structure of claim 8, wherein the incline of the top surface of the first conductive layer and the first inclined top surface of the second conductive layer are collinear and have a same slope.
 10. The semiconductor structure of claim 1, wherein the hard mask layer is in contact with a top surface of the first conductive layer, wherein the top surface of the first conductive layer is substantially parallel a top surface of the semiconductor substrate.
 11. A semiconductor structure, comprising: a fin structure extending from a semiconductor substrate; a gate stack structure formed over the fin structure, wherein the gate stack structure includes: a gate dielectric layer having a U-shape in a cross-sectional view, the U-shape defined by a first bottom portion and two opposing side portions; a first work function layer formed over the gate dielectric layer, wherein the first work function layer has a second bottom portion interfacing the first bottom portion of the U-shape of the gate dielectric layer and two opposing side portions interfacing each interfacing a side portion of the two opposing side portions of the U-shape of the gate dielectric layer; a second work function layer disposed over the first work function layer and having a sloped top surface extending downward from each of the two opposing sidewall portions of the first work function layer toward the bottom portion of the first work function layer; and a hard mask layer over the second work function layer, wherein the hard mask layer interfaces the gate dielectric layer.
 12. The semiconductor structure of claim 11, wherein the hard mask layer also interfaces the first work function layer.
 13. The semiconductor structure of claim 11, wherein an additional conductive layer interposes the second work function layer and the hard mask layer.
 14. The semiconductor structure of claim 13, wherein the additional conductive layer interfaces the sloped top surfaces of the second work function layer.
 15. The semiconductor structure of claim 14, wherein the additional conductive layer extends to interface a planar surface of the second work function layer, the planar surface extending between the sloped top surfaces of the second work function layer.
 16. A semiconductor structure, comprising: a gate structure formed over a semiconductor substrate, wherein the gate structure comprises: a gate dielectric layer; a first work function layer over the gate dielectric layer; a second work function layer over the first work function layer, wherein the second work function layer has a different composition than the first work function layer, and wherein the second work function layer has a bottom portion, a first side portion and a second side portion, wherein the first side portion and the second side portion extend above the bottom portion, and wherein the first side portion has an uppermost surface that is disposed at an incline and the second side portion has an uppermost surface that is disposed at an incline, the inclines of the first side portion and the second side portion extending downward toward the bottom portion from adjacent the first work function layer; another conductive material interposing the first side portion and the second side portion above the bottom portion of the second work function layer; and a hard mask layer being in contact with at least one of the first work function layer or the gate dielectric layer.
 17. The semiconductor structure of claim 16, wherein the hard mask layer is in contact with each of the first work function layer and the gate dielectric layer.
 18. The semiconductor structure of claim 16, wherein the hard mask layer is in contact with a sidewall of the gate dielectric layer and a top surface of the first work function layer.
 19. The semiconductor structure of claim 16, wherein the hard mask layer has a top surface substantially coplanar with a top surface of the gate dielectric layer.
 20. The semiconductor structure of claim 16, wherein the another conductive material interfaces the hard mask layer, the first work function layer, the second work function layer, and the gate dielectric layer. 